Surface Resistivity E3-E4 Polypropylene

• Customization: Available
• Material: Polypropylene/PP
• Usage: Engineering Plastics, Specialty Plastics
• Model NO.: PP-C20
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: Black
• Carbon Fiber Content: 20%
• Tensile Strength: 39MPa
• Elongation: 50%
• Flexural Modulus: 5.66gpa
• 3.2mm Izod Notched Impact Strength: 5.6kj/M2
• Surface Resistivity: 10e3-10e4 Ohm/Sq
• Transport Package: 20kg Bag
• Specification: 20% carbon fiber
• Trademark: XIANGU
• Origin: China
• HS Code: 3902100090
• Production Capacity: 5000ton/Year

Product Description

Conductive Polypropylene
20% Carbon Fiber PP
Surface Resistivity E3-E4 Polypropylene

Conductive PP granule PP-C20 was a kind of compound material with 20% carbon fiber by extruding technique.It has excellent conductive property,good heat resistance and cold resistance,abrasive resistance,chemical stability,good mechanical strength,anti-static property.resistance to environmental stress cracking.good hardness,high tensile strength.etc.

SPECIFICATIONS:

Model:	PP-C20
Color:	black
Carbon fiber content(%):	20
Density(g/cm3):	1.2
Shrinkage-flow(%):	0.3-0.4
Tensile strength(Mpa ):	39
Elongation(% ):	50
Flexural modulus(Gpa):	5.66
3.2mm IZOD notched impact strength(KJ/m^2):	5.6
Flame Rating-UL:	HB
Surface resistivity(ohm/sq):	10E3-10E4
Baking temperature(ºC):	85ºC 2-4h
Injection or extrusion temperature(ºC):	190-230ºC

STORAGE:
The conductive PP granule should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.

PACKAGING:


PRODUCT DETAILS: