200D para-aramid filament is a new high-tech synthetic fiber.This fiber has high strength and modulus, strong hydrogen bonding strength,strength up to 20 g/d or more,the strength is 5-6 times of steel wire,modulus is 2-3 times of fiberglass,toughness is 2 times of the steel wire,but the weight is only 1/5 of the steel wire.Continuous using temperature range is extremely wide,long run in the range of -196ºC to 204ºC.No decomposition and melting at 560ºC.Strength can maintain 75% undergo 100 hours at 200ºC.It can resist chemical solvent,acid and alkali,anti-aging,good adhesion to rubber.It is suitable as a reinforcing fiber used in various composite materials,bulletproof products,building materials,special protective clothing,electronics equipment,friction and sealing materials etc.Usually it is used as a protective material,widely used in bullet-proof vests,ballistic helmets,bullet-proof armor,bullet-proof panels.Also as a reinforcing material widely used in rubber,thermoplastics,thermosetting plastics,various high-temperature composite structures,brake pads,clutch linings,friction plate,wear-resistant fillers.
SPECIFICATIONS:
| Model: |
XGPAF200 |
| Fiber type: |
Para-aramid |
| Density: |
1.47g/cm3 |
| Mono filament linear density: |
1.5D/1.67tex |
| Filament linear density: |
200D |
| Mono filament diameter: |
12μm |
| Mono filament number: |
134pcs |
| Net weight per bobbin: |
2kg |
| Fiber length: |
45000m/kg |
| Specific volume resistance: |
5x1015Ω.cm |
| Moisture: |
4%-8% |
| Tenacity at break: |
20.83cN/dtex |
| Modulus: |
80GPa-102GPa |
| Elongation at break: |
3.0%-3.7% |
APPLICATION FIELDS:
mainly used for reinforcing fiber for headphone wire,optical cable,electric wire.etc.
STORAGE:
The para-aramid filament should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire
PACKAGING:
PRODUCT DETAIL IMAGES: