Kevlar Chopped Fiber

Contact Supplier

Gold Member Since 2016

Suppliers with verified business licenses

Manufacturer/Factory

Basic Info.

Model NO.
XGPF1210
Width
1.2D
Function
High Strength Fiber
Structure
Miscellaneous Chain Synthetic
Model
Xgpf1210
Colors
Yellowish
Fiber
PARA-Aramid
Density
1.47g/cm3
P-Aramid Content
100%
Average Fiber Length
10mm
Tensile Strength
19.4-21 Cn/Dtex
Tensile Modulus
80gpa~120gpa
Elongation at Break
2.5%-3.84%
Moisture
<0.2%
Transport Package
5kg Per Bag
Specification
ROHS
Trademark
XIANGU
Origin
Guangdong
HS Code
54021190
Production Capacity
500000kg

Product Description

10mm kevlar chopped fiber was chopped in 10mm by a special cutting equipment. This fiber has high strength and modulus, strong hydrogen bonding strength, strength up to 28 g/d or more, strength is 5-6 times of steel wire.specific modulus 2-3 times of it,toughness 2 times of it while weight is just 1/5 of the wire.Continuous using temperature range is extremely wide, long running in the range of -196 ºC to 204 ºC,no decomposition and melting at high temperature of 560 ºC,strength can maintain 75% through 100 hours at 200 ºC.also has good chemical solvent resistance, resisting acid and alkali, anti-aging, good adhesion to rubber. Usually it is used as a reinforcing material in the fields of thermoplastics, thermosetting plastics, high-temperature composite structures, brake pads, clutch linings, friction material, wear-resistant filler, cable sheathing, gaskets, slot insulation, phase insulation barrier, interturn insulation and so on.
 
SPECIFICATIONS:
Model:XGPF1210
Color:yellowish
Fiber type:Para-aramid
Density(g/cc)1.47
Linear density of mono filament(D) 1.5
Filament diameter(μm)12
Fiber length(mm)10
Tensile strength( cN/dtex)19.4-21
Elongation at break(%)2.5-3.84
Tensile modulus(GPa)80~120
Shrinkage(%)<0.2(190ºC×15m)
Moisture (%):<0.2
APPLICATION FIELDS:
1.Engineering Plastics,thermosetting resin,friction materials, automotive brakes,composite materials and Kevlar reinforced paper. 
2.reinforcing materials,construction,rubber,reinforced cable,cable and other high-intensity rope.
3.composite material with resin or rubber,can significantly reduce the weight,increase loading weight,suitable for the production of aerospace equipment,high-speed trains and yachts shell.
4.Friction and sealing materials,friction materials reinforced fiber, significantly improved wear resistance,suitable for high temperature conditions.
 
STORAGE:
The 10mm kevlar chopped fiber should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire

PACKAGING:
Kevlar Chopped Fiber

 
SHIPMENT AND TRANSPORTATION:
1.Shipment by sea:for sea transportation,generally 20 pallets(each 180kg.two layers)be loaded into 20 feet container.total net weight is 2400kg.
2.transportation by truck:for truck transportation,generally loading in buck with 7layers,about 3120kg
3.transportation by rail:for rail transportation,generally loading in buck,about 6720kg.
 
PRODUCT DETAIL IMAGES:
Kevlar Chopped FiberKevlar Chopped FiberKevlar Chopped FiberKevlar Chopped Fiber
Kevlar Chopped Fiber

Send your message to this supplier

*From:
*To:
avatar Mr. Bulin Tang
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

You Might Also Like

Contact Supplier

Gold Member Since 2016

Suppliers with verified business licenses

Manufacturer/Factory
Registered Capital
8000000 RMB
Plant Area
>2000 square meters