Low Surface Resistivity Nylon

• Material: Polyamide(Nylon 6.66)/PA
• Usage: Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: Black
• Carbon Fiber Content: 30%
• Model NO.: PA66-C30
• Tensile Strength: 230MPa
• Elongation: 4%
• Flexural Modulus: 19.8gpa
• 3.2mm Izod Notched Impact Strength: 17.5kj/M2
• Surface Resistivity: 10e3 Ohm/Sq
• Transport Package: 20kg Bag
• Specification: 30% carbon fiber
• Trademark: XIANGU
• Origin: China
• HS Code: 3908101190
• Production Capacity: 5000ton/Year

Product Description

low Surface Resistivity Nylon
30% Carbon Fiber Nylon 66
Conductive PA66 granule PA66-C30 was a kind of compound material with 30% carbon fiber by extruding technique.It has excellent conductive property,good heat resistance and cold resistance,abrasive resistance,chemical stability,good mechanical strength,anti-static property.resistance to environmental stress cracking.good hardness,high tensile strength.etc.

SPECIFICATIONS:

Model:	PA66-C30
Color:	black
Carbon fiber content(%):	30
Density(g/cm3):	1.3
Shrinkage-flow(%):	0.2-0.3
Tensile strength(Mpa ):	230
Flexural strength(Mpa):	335
Elongation(% ):	2-4
Flexural modulus(Gpa):	19.8
3.2mm IZOD notched impact strength(KJ/m^2):	17.5
Heat distortion temperature(ºC):	250
Flame Rating-UL:	HB
Surface resistivity(ohm/sq):	10E3
Baking temperature(ºC):	110ºC 2-4h
Injection or extrusion temperature(ºC):	250-280ºC

STORAGE:
The conductive PA66 granule should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.