12K T700 Carbon Fiber Pan Precursor

• Customization: Available
• Application Field: Carbon Fiber
• Colour: White
• Model NO.: XG-12K
• Luster: Semi-Dull
• Property: Abrasion Resistance, Acid and Alkali Resistance, Chemical Corrosion Resistance, Flame Retardancy, Heat Resistance, Tear Resistance
• Model: Xg-12K
• Filament Number: 12K
• Linear Density: 1440tex
• Linear Density of Monofilament: 0.122+/-0.003tex
• Linear Density Deviation From Nominal: Max.+/-5%
• Tensile Strenght for Single Fiber: Min.73cn/Tex
• Elongation at Break: 13+/-4%
• Oil Content: 1.2+/-0.5%
• Humidity: <0.1%
• Material: 100% Acrylic
• Fiber Type: Filament
• Color: White
• Transport Package: Pallet
• Specification: ROHS
• Trademark: XIANGU
• Origin: Guangdong
• HS Code: 5402699000
• Production Capacity: 500000000kg

Product Description

12k T700 Carbon Fiber PAN Precursor Polyacrylonitrile fiber precursor is high purity and high strength fiber through dry jet wet spinning with surface finishing size treatment.It has higher elastic modulus,tensile strength and anti-UV properties,anti-high temperature and cold performance.It is the best raw material of PAN carbon fiber Via Pre-oxidation(200~300ºC),carbonization(1000~1500ºC), Graphitization(2500~3000ºC).Generally produce T700 or 4900Mpa carbon fiber filament.

SPECIFICATIONS:

MODEL:	XG-12K
FILAMENT NUMBER	12K
LINEAR DENSITY	1440tex
LINEAR DENSITY OF MONOFILAMENT	0.122±0.003tex
LINEAR DENSITY DEVIATION FROM NOMINAL	Max.±5%
TENSILE STRENGHT FOR SINGLE FIBER	Min.73 cN/tex
ELONGATION AT BREAK	13±4%
OIL CONTENT	1.2±0.5%
HUMIDITY	≤0.15%

STORAGE:
The T700 polyacrylonitrile precursor should be keep dry in their original cartons and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.