HDPE Surface Resistivity 10e2-10e3

• Customization: Available
• Material: High Density Polyethylene/HDPE
• Usage: Engineering Plastics, Specialty Plastics
• Model NO.: HDPE-C30
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: Black
• Carbon Fiber Content: 30%
• Tensile Strength: 52MPa
• Elongation: 76%
• Flexural Modulus: 4.36gpa
• 3.2mm Izod Notched Impact Strength: 5.8kj/M2
• Surface Resistivity: E2-E3ohm/Sq
• Transport Package: 20kg Bag
• Specification: 30% carbon fiber
• Trademark: XIANGU
• Origin: China
• HS Code: 3901200001
• Production Capacity: 5000ton/Year

Product Description

HDPE Surface Resistivity 10E2-10E3/30% Carbon Fiber HDPE/Conductive High density polyethylene/HDPE granule HDPE-C30 was a kind of compound material with 30% carbon fiber by extruding technique.It has excellent conductive property,good heat resistance and cold resistance,chemical stability,good mechanical strength,anti-static property.resistance to environmental stress cracking.Hardness, tensile strength and creep are better than low density polyethylene.

SPECIFICATIONS:
 

Model:	HDPE-C30
Color:	black
Carbon fiber content(%):	30
Density(g/cm3):	1.05
Shrinkage-flow(%):	0.4-0.8
Tensile strength(Mpa ):	52
Elongation(% ):	76
Flexural modulus(GPA):	4.36
3.2mm IZOD notched impact strength(KJ/m^2):	5.8
Flame Rating-UL:	HB
Surface resistivity(ohm/sq):	10E2-10E3
Baking temperature(ºC)::	80ºC 2-4h
Injection or extrusion temperature(ºC):	180-220ºC

STORAGE:
The HDPE granule should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.